Mechanical properties of boards made in biocomposites reinforced with wood and Posidonia oceanica fibers
Empreu sempre aquest identificador per citar o enllaçar aquest ítem
http://hdl.handle.net/10045/63200
Títol: | Mechanical properties of boards made in biocomposites reinforced with wood and Posidonia oceanica fibers |
---|---|
Autors: | Maciá Mateu, Antonio | Baeza, F. Javier | Saval Pérez, José Miguel | Ivorra, Salvador |
Grups d'investigació o GITE: | Grupo de Ensayo, Simulación y Modelización de Estructuras (GRESMES) | Materiales y Sistemas Constructivos de la Edificación | Durabilidad de Materiales y Construcciones en Ingeniería y Arquitectura | Tecnología de Materiales y Territorio (TECMATER) |
Centre, Departament o Servei: | Universidad de Alicante. Departamento de Ingeniería Civil |
Paraules clau: | Biocomposites | Posidonia oceanica | Recycling | Mechanical properties | Structural boards |
Àrees de coneixement: | Mecánica de Medios Continuos y Teoría de Estructuras | Ingeniería de la Construcción |
Data de publicació: | 1-de novembre-2016 |
Editor: | Elsevier |
Citació bibliogràfica: | Composites Part B: Engineering. 2016, 104: 1-8. doi:10.1016/j.compositesb.2016.08.018 |
Resum: | The development of biocomposites has valorized some natural products related to natural processes or crop industries. In this regard, Posidonia oceanica is a marine phanerogam typical of Mediterranean coasts, in which due to tourism industry a lot of resources are destined to remove and treat Posidonia residues left on beaches. In this work an alternative to recycle this natural waste has been studied. Biocomposites with Posidonia and pine-wood particles were tested as an alternative to structural wood particle boards used in construction. Different substitution ratios (pine by Posidonia) were prepared in two different polymeric matrices and their mechanical properties were tested. Particles boards made in 75% Posidonia oceanica and 25% wood particles and a MDI matrix (20–30% by fibers mass) showed the best strength and stiffness to density ratios. This stiffness was even similar to a panel made totally in wood and MDI in the same dosage, i.e. 75% of pine fibers could be replaced by Posidonia with low stiffness loss. |
Patrocinadors: | The authors would like to thank the University of Alicante for its financial support, VIBGROB-212-(GRESMES). |
URI: | http://hdl.handle.net/10045/63200 |
ISSN: | 1359-8368 (Print) | 1879-1069 (Online) |
DOI: | 10.1016/j.compositesb.2016.08.018 |
Idioma: | eng |
Tipus: | info:eu-repo/semantics/article |
Drets: | © 2016 Elsevier Ltd. |
Revisió científica: | si |
Versió de l'editor: | http://dx.doi.org/10.1016/j.compositesb.2016.08.018 |
Apareix a la col·lecció: | INV - GRESMES - Artículos de Revistas INV - DMCIA - Artículos de Revistas INV - MSCE - Artículos de Revistas INV - TECMATER - Artículos de Revistas |
Arxius per aquest ítem:
Arxiu | Descripció | Tamany | Format | |
---|---|---|---|---|
2016_Macia_etal_CompositesB_final.pdf | Versión final (acceso restringido) | 1,12 MB | Adobe PDF | Obrir Sol·licitar una còpia |
2016_Macia_etal_CompositesB_accepted.pdf | Accepted Manuscript (acceso abierto) | 1,07 MB | Adobe PDF | Obrir Vista prèvia |
Tots els documents dipositats a RUA estan protegits per drets d'autors. Alguns drets reservats.