Production of bamboo-type carbon nanotubes doped with nitrogen from polyamide pyrolysis gas
Empreu sempre aquest identificador per citar o enllaçar aquest ítem
http://hdl.handle.net/10045/73733
Títol: | Production of bamboo-type carbon nanotubes doped with nitrogen from polyamide pyrolysis gas |
---|---|
Autors: | Arnaiz Arnaiz, Noelia | Martin-Gullon, Ignacio | Font, Rafael | Gómez-Rico, María Francisca |
Grups d'investigació o GITE: | Residuos, Energía, Medio Ambiente y Nanotecnología (REMAN) |
Centre, Departament o Servei: | Universidad de Alicante. Departamento de Ingeniería Química |
Paraules clau: | BCNTs | Chemical vapor deposition | Polyamide 6.6 | Pyrolysis |
Àrees de coneixement: | Ingeniería Química |
Data de publicació: | de març-2018 |
Editor: | Elsevier |
Citació bibliogràfica: | Journal of Analytical and Applied Pyrolysis. 2018, 130: 52-61. doi:10.1016/j.jaap.2018.01.027 |
Resum: | Bamboo-type carbon nanotubes (BCNTs) doped with nitrogen were produced by catalytic chemical vapor deposition from the effluent gases resulting from pyrolysis of polyamide 6.6. This polymer provides the carbon and nitrogen source and allows to obtain enough hydrogen during its decomposition for the carbon nanotubes (CNTs) production without prior catalyst reduction. The influence of pyrolysis and growth temperatures was studied in order to obtain the best quality CNTs. Transmission electron microscopy, X-ray diffraction, and Raman spectrometry showed that the best results were obtained at 900 °C pyrolysis temperature and 750 °C growth temperature, since the presence of amorphous carbon was negligible and the best crystalline degree was obtained. These BCNTs had from 5 to 20 layers and their arcs of bamboo-like compartments had from 3 to 15 layers. They had 20 nm in diameter and lengths typically on the order of micrometers. |
Patrocinadors: | This work was supported by the Spanish Ministry of Science and Innovation [CTQ 2008-05520 project], the Spanish Ministry of Economy, Industry and Competitiveness [CTQ 2013-44213-R project] and the Valencian Community Government (Spain) [Prometeo/2009/043/FEDER and PrometeoII/2014/007 projects]. |
URI: | http://hdl.handle.net/10045/73733 |
ISSN: | 0165-2370 (Print) | 1873-250X (Online) |
DOI: | 10.1016/j.jaap.2018.01.027 |
Idioma: | eng |
Tipus: | info:eu-repo/semantics/article |
Drets: | © 2018 Elsevier B.V. |
Revisió científica: | si |
Versió de l'editor: | http://dx.doi.org/10.1016/j.jaap.2018.01.027 |
Apareix a la col·lecció: | INV - REMAN - Artículos de Revistas |
Arxius per aquest ítem:
Arxiu | Descripció | Tamany | Format | |
---|---|---|---|---|
2018_Arnaiz_etal_JAAP_final.pdf | Versión final (acceso restringido) | 2,63 MB | Adobe PDF | Obrir Sol·licitar una còpia |
2018_Arnaiz_etal_JAAP_accepted.pdf | Accepted Manuscript (acceso abierto) | 3,15 MB | Adobe PDF | Obrir Vista prèvia |
Tots els documents dipositats a RUA estan protegits per drets d'autors. Alguns drets reservats.